Method For Fabricating Heterogeneous Nickel-Based Catalyst On Aluminum Oxide Support, Heterogeneous Nickel-Based Catalyst On Aluminum Oxide Support And Method For Synthesizing Polyetheramine

ABSTRACT

The present disclosure provides a method for fabricating a heterogeneous nickel-based catalyst on an aluminum oxide support. The method includes a solution preparation step, a drop-cast step, a first calcining step, and a second calcining step. The solution preparation step is provided for preparing a precursor solution. The drop-cast step is provided for dropping the precursor on the support. The first calcining step is provided for obtaining an oxidation state catalyst. The second calcining step is provided for obtaining the heterogeneous nickel-based catalysts on aluminum oxide support.

RELATED APPLICATIONS

This application claims priority to Taiwan Application Serial Number 107139368, filed Nov. 6, 2018, which is herein incorporated by reference.

BACKGROUND Technical Field

The present disclosure relates to a method for fabricating catalysts. More particularly, the present disclosure relates to a method for fabricating a heterogeneous nickel-based catalyst on an aluminum oxide support, a heterogeneous nickel-based catalyst on an aluminum oxide support thereof and a method for synthesizing polyetheramine thereof.

Description of Related Art

Polyetheramines (PEA) are the important chemical raw materials and extensively used as intermediates for the production of petrochemicals, such as household chemicals, pesticides and pharmaceuticals. The reductive amination reaction of polypropylene glycol (PPG) is catalyzed by the heterogeneous catalysts so as to produce polyetheramines with the desired selectivity recognized as one of the effective production routes.

At the present, the heterogeneous catalysts are considered as a key technology for the production of the high-value petrochemical products, which are beneficial as the industrial-scale production materials. Among many catalysts, the nickel-based catalysts are extensively considered as one of the ideal catalyst materials due to the characteristics, such as high activity, high selectivity and low cost. Now, Raney nickel is mainly used as the catalyst, but the long-term stability of Raney nickel is not good.

Therefore, how to prepare the composite heterogeneous catalysts so as to achieve high activity, high selectivity and high stability for catalyzing the reductive amination reaction of polypropylene glycol (PPG) is the goal of the relevant industry.

SUMMARY

According to one aspect of the present disclosure, a method for fabricating a heterogeneous nickel-based catalyst on an aluminum oxide support includes steps as follows. A solution preparation step is performed, wherein a catalytically active precursor is used as a precursor solution, and the precursor solution contains a nickel ion. A drop-cast step is performed, wherein the precursor solution is dropped on a support so as to obtain a catalyst precursor, and the support is an aluminum oxide support. A first calcining step is performed, wherein the catalyst precursor is calcined so as to obtain an oxidation state catalyst. A second calcining step is performed, wherein the oxidation state catalyst is calcined under a reducing gas so as to obtain the heterogeneous nickel-based catalyst on the aluminum oxide support, and the reducing gas is hydrogen.

According to another aspect of the present disclosure, a heterogeneous nickel-based catalyst on an aluminum oxide support is provided. The heterogeneous nickel-based catalyst on the aluminum oxide support is fabricated by the method according to the aforementioned aspect.

According to further another aspect of the present disclosure, a method for synthesizing polyetheramine includes steps as follows. A heterogeneous nickel-based catalyst on an aluminum oxide is provided, wherein the heterogeneous nickel-based catalyst on the aluminum oxide is fabricated by the method according to the aforementioned aspect. A reductive amination reaction of polypropylene glycol step is performed, wherein polypropylene glycol is performed the reductive amination reaction by the heterogeneous nickel-based catalyst on the aluminum oxide support used as a catalyst so as to obtain polyetheramine at an environment contained hydrogen and ammonia.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure can be more fully understood by reading the following detailed description of the embodiment, with reference made to the accompanying drawings as follows:

FIG. 1 is a flow chart of a method for fabricating a heterogeneous nickel-based catalyst on an aluminum oxide support according to one embodiment of the present disclosure.

FIG. 2 is a flow chart of a method for synthesizing polyetheramine according to another embodiment of the present disclosure.

FIG. 3A is an XRD diffractogram of the Ni@Al₂O₃ with the different Ni concentrations.

FIG. 3B is a FESEM image of the Ni@Al₂O₃ with the different Ni concentrations.

FIG. 4 is a H₂-TPR profile of the Ni@Al₂O₃ with the different Ni concentrations.

FIG. 5A is an XRD diffractogram of the Ni—CeO₂@Al₂O₃ with the different Ce concentrations.

FIG. 5B is a FESEM image of the Ni—CeO₂@Al₂O₃ with the different Ce concentrations.

FIG. 6 is a H₂-TPR profile of the Ni—CeO₂@Al₂O₃ with the different Ce concentrations.

FIG. 7A is an XRD diffractogram of the Ni@Al₂O₃ according to Example 2, Example 3, Example 9 and Example 10 of the present disclosure.

FIG. 7B is an XRD diffractogram of the Ni—CeO₂@Al₂O₃ according to Example 6, Example 11 and Example 12 of the present disclosure.

FIG. 8 is a H₂-TPR profile of the Ni@Al₂O₃ and the Ni—CeO₂@Al₂O₃ after the passivation step.

FIG. 9 is a schematic view for the reaction mechanism of the reductive amination reaction of polypropylene glycol catalyzed by the Ni@Al₂O₃.

FIG. 10 is a schematic view for the reaction mechanism of the reductive amination reaction of polypropylene glycol catalyzed by the Ni—CeO₂@Al₂O₃.

FIG. 11A is a histogram for the conversion ratio of PPG of the Ni@Al₂O₃ according to Example 1 to Example 4 of the present disclosure.

FIG. 11B is a histogram for the turnover frequency of the Ni@Al₂O₃ according to Example 1 to Example 4 of the present disclosure.

FIG. 11C is a histogram for the selectivity to primary amine of the Ni@Al₂O₃ according to Example 1 to Example 4 of the present disclosure.

FIG. 12A is a histogram for the conversion ratio of PPG of the Ni—CeO₂@Al₂O₃ according to Example 2, Example 5 to Example 8 of the present disclosure.

FIG. 12B is a histogram for the turnover frequency of the Ni—CeO₂@Al₂O₃ according to Example 2, Example 5 to Example 8 of the present disclosure.

FIG. 12C is a histogram for the selectivity to primary amine of the Ni—CeO₂@Al₂O₃ according to Example 2, Example 5 to Example 8 of the present disclosure.

FIG. 13A is a histogram for the conversion ratio of PPG and the selectivity to primary amine of the Ni@Al₂O₃ according to Example 2 and Example 9 of the present disclosure.

FIG. 13B is a histogram for the conversion ratio of PPG and the selectivity to primary amine of the Ni—CeO₂@Al₂O₃ according to Example 6, Example 11 and Example 12 of the present disclosure.

FIG. 13C is a histogram for the conversion ratio of PPG and the selectivity to primary amine of the Ni@Al₂O₃ according to Example 3 and Example 10 of the present disclosure.

FIG. 14A is an XRD diffractogram of the Ni@Al₂O₃ after the reductive amination reaction.

FIG. 14B is an XRD diffractogram of the Ni—CeO₂@Al₂O₃ after the reductive amination reaction.

FIG. 15A is a histogram for the conversion ratio of PPG and the selectivity to primary amine from the first and the second test according to Example 2 of the present disclosure.

FIG. 15B is a histogram for the conversion ratio of PPG and the selectivity to primary amine from the first and the second test according to Example 6 of the present disclosure.

DETAILED DESCRIPTION

The present disclosure will be further exemplified by the following specific embodiments. However, the embodiments can be applied to various inventive concepts and can be embodied in various specific ranges. The specific embodiments are only for the purposes of description, and are not limited to these practical details thereof.

Please refer to FIG. 1, which is a flow chart of a method for fabricating a heterogeneous nickel-based catalyst on an aluminum oxide support 100 according to one embodiment of the present disclosure. It should be noted that the method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support is mainly prepared by the incipient wetness impregnation. The method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support 100 includes a step 110, a step 120, a step 130 and a step 140.

First, in the step 110, a solution preparation step is performed, wherein a catalytically active precursor is used as a precursor solution, and the precursor solution contains a nickel ion. Specifically, the catalytically active precursor can be a nickel nitrate solution or a cerium nitrate solution, and the precursor solution can be the nickel nitrate solution or a mixed solution of nickel nitrate and cerium nitrate. The heterogeneous nickel-based catalyst on the aluminum oxide support is prepared by the different type and the different concentration composition of the precursor solution.

Next, in the step 120, a drop-cast step is performed, wherein the precursor solution is dropped on a support so as to obtain a catalyst precursor, and the support is an aluminum oxide support. The aluminum oxide support is dried at a temperature of 353 K to 393 K first, and reserved overnight.

In the step 130, a first calcining step is performed, wherein the catalyst precursor is calcined so as to obtain an oxidation state catalyst, and the temperature of the first calcining step can range from 300° C. to 400° C.

Then, in the step 140, a second calcining step is performed, wherein the oxidation state catalyst is calcined under a reducing gas so as to obtain the heterogeneous nickel-based catalyst on the aluminum oxide support, and the reducing gas is hydrogen. The temperature of the second calcining step can range from 250° C. to 400° C. Furthermore, after the second calcining step, a passivation step can be further included. The heterogeneous nickel-based catalyst on the aluminum oxide support is cooled at the temperature of 200° C. to 400° C. with nitrogen, and then passivated at the temperature of 180° C. to 220° C. by introducing an air.

Therefore, the present disclosure further provides the heterogeneous nickel-based catalyst on the aluminum oxide support fabricated by the aforementioned method, which can be used to catalyze the reductive amination reaction of polypropylene glycol to synthesize polyetheramine. Furthermore, the heterogeneous nickel-based catalyst on the aluminum oxide support further includes adding CeO₂ as a co-catalyst. The addition of the co-catalyst component to the catalyst can cause the concerted reaction at the interface between the metal and the support so as to enhance the activity and the stability of the catalyst. Then the heterogeneous nickel-based catalyst on the aluminum oxide support can be prepared by controlling a Ni concentration and a Ce concentration, wherein the heterogeneous nickel-based catalyst on the aluminum oxide support can be a nickel catalyst on the aluminum oxide support (hereinafter referred to as Ni@Al₂O₃) or a nickel-cerium oxide catalyst on the aluminum oxide support (hereinafter referred to as Ni—CeO₂@Al₂O₃). A range of the Ni concentration of the Ni@Al₂O₃ can be greater than 0 wt % and less than or equal to 40 wt %. The range of the Ni concentration of the Ni—CeO₂@Al₂O₃ can be greater than 0 wt % and less than or equal to 25 wt %, and the range of the Ce concentration can be greater than 0 wt % and less than or equal to 25 wt %.

Hereinafter, a method for synthesizing polyetheramine 200 using the aforementioned heterogeneous nickel-based catalyst on the aluminum oxide support will be further described with FIG. 2. The method for synthesizing polyetheramine 200 includes a step 210 and a step 220.

First, in the step 210, the heterogeneous nickel-based catalyst on the aluminum oxide support is provided, wherein the heterogeneous nickel-based catalyst on the aluminum oxide support can be the Ni@Al₂O₃ and the Ni—CeO₂@Al₂O₃.

Next, in the step 220, a reductive amination reaction of polypropylene glycol step is performed, wherein polypropylene glycol is performed the reductive amination reaction by the aforementioned heterogeneous nickel-based catalyst on the aluminum oxide support used as the catalyst, so as to obtain polyetheramine at an environment contained hydrogen and ammonia. A molar ratio of hydrogen (H₂) to polypropylene glycol (PPG) can be range from 1 to 1.5, and a molar ratio of ammonia (NH₃) to polypropylene glycol (PPG) can be range from 38 to 40.6. The details of the step 220 will be described in the subsequent embodiments, and will not be described herein.

Hereinafter, the specific examples and the comparative examples are described to explain the detail of the heterogeneous nickel-based catalyst on the aluminum oxide support, the preparation method thereof, and the method for synthesizing polyetheramine thereof used to achieve the effects which are provided in the present disclosure.

Example 1. A Material Properties Analysis of a Heterogeneous Nickel-Based Catalyst on an Aluminum Oxide Support

A heterogeneous nickel-based catalyst on an aluminum oxide support of the present disclosure is prepared by a step 110 to a step 140 of a method for fabricating a heterogeneous nickel-based catalyst on an aluminum oxide support 100 of FIG. 1. First, a catalytically active precursor is prepared as a precursor solution. The catalytically active precursor of the present disclosure is a nickel nitrate solution or a cerium nitrate solution, and the precursor solution is the nickel nitrate solution or a mixed solution of nickel nitrate and cerium nitrate.

Next, the aforementioned precursor solution is used a drop-cast to load on the aluminum oxide support so as to obtain a catalyst precursor, wherein the aluminum oxide support is dried at a temperature of 373K first, and reserved overnight. Then, the catalyst precursor is calcined at 350° C. for 3 hours under an air, and calcined at 250° C. or 400° C. for 1 hour under hydrogen so as to obtain the heterogeneous nickel-based catalyst on the aluminum oxide support. After the second calcination, the heterogeneous nickel-based catalyst on the aluminum oxide support is cooled at the temperature of 200° C. to 400° C. with nitrogen, and passivated at the temperature of 200° C. by introducing the air. The heterogeneous nickel-based catalyst on the aluminum oxide support fabricated by the aforementioned method can be a nickel catalyst on the aluminum oxide support (hereinafter referred to as Ni@Al₂O₃) or a nickel-cerium oxide catalyst on the aluminum oxide support (hereinafter referred to as Ni—CeO₂@Al₂O₃).

The heterogeneous nickel-based catalyst on the aluminum oxide support of the present disclosure can be controlled the crystallite size of the active metal and the metal surface area by controlling the composition (the type of the precursor and the concentration) and the operating condition (the calcining temperature) to achieve the high catalytic activity, the selectivity and the stability of the heterogeneous nickel-based catalyst on the aluminum oxide support. The crystallite size of the heterogeneous nickel-based catalyst on the aluminum oxide support is analyzed by using the X-ray diffraction (XRD). The particle size and the morphology of the heterogeneous nickel-based catalyst on the aluminum oxide support are analyzed by using the field emission scanning electron microscope (FESEM). The metal surface area and the specific surface area of the heterogeneous nickel-based catalyst on the aluminum oxide support are analyzed by using the specific surface area and porosity analyzer and the chemisorption analyzer. The activity test, the selectivity test and the stability test are performed by the aforementioned analysis.

1.1 an Effect of the Ni Concentration Loading on the Material Properties of the Ni@Al₂O₃

Example 1 to Example 4 of the present disclosure are observed the effect of the Ni concentration loading on the material properties of the Ni@Al₂O₃ by the different Ni concentrations. The controlling conditions of the Ni@Al₂O₃ are shown in Table 1, wherein C_(Ni) and C_(Ce) represent the concentrations of Ni and Ce, T_(d2) represents the second calcining temperature, and T_(pas) represents the surface passivation temperature.

TABLE 1 The controlling conditions of the Ni@Al₂O₃ Ni@Al₂O₃ C_(Ni) (wt %) C_(Ce) (wt %) T_(d2) (° C.) T_(pas) (° C.) Example 1 5 0 400 N/A Example 2 15 0 400 N/A Example 3 25 0 400 N/A Example 4 40 0 400 N/A

Please refer to FIGS. 3A and 3B. FIG. 3A is an XRD diffractogram of the Ni@Al₂O₃ with the different Ni concentrations. FIG. 3B is a FESEM image of the Ni@Al₂O₃ with the different Ni concentrations. As shown in FIG. 3A, the crystalline phase of metallic Ni is presented in Example 2 to Example 4, and the crystallite size of Ni (d_(Ni)) can be estimated by analyzing the waveform of the X-ray diffraction peak. The crystallite sizes of Ni (d_(Ni)) of Example 2 to Example 4 are shown in Table 2. As shown in FIG. 3B, the Ni particles are dispersed on the surface of the aluminum oxide support, and the particle sizes of Ni are obtained by the histogram analysis. The particle sizes of Ni of Example 1 to Example 4 are shown in Table 2. The results indicate that when C_(Ni) increases, the d_(Ni) and the particle size of Ni of the Ni@Al₂O₃ will increase. Furthermore, C_(Ni) of Example 1 is too low to identify the crystalline phase and crystallite size of Ni by XRD diffraction.

TABLE 2 The crystallite sizes and the particle sizes of Ni of the Ni@Al₂O₃ Ni@Al₂O₃ d_(Ni) (nm) particle size of Ni (nm) Example 1 N/A 16.4 Example 2 5.3 25.8 Example 3 7.2 80.1 Example 4 10.1 101.8

Furthermore, the analysis of the specific surface area (S_(BET)), the pore size (d_(pore)) and the metal surface area (S_(msa)) of Example 1 to Example 4 are ore, shown in Table 3. As shown in Table 3, by increasing C_(Ni), the specific surface area of the Ni@Al₂O₃ is deceased from 192.8 m²/g to 105.6 m²/g, and the metal surface area is increased from 2.0±0.6 m²/g to 4.4 m²/g. However, when C_(Ni) is increased to 40 wt %, the metal surface area is decreased to 0.88±0.06 m²/g substantially. The results indicate that the decrease of the specific surface area is attributed to the increase of C_(Ni) so as to cause the deposition of Ni in the mesoporous of the aluminum oxide support. Furthermore, in the case of the high concentration of Ni, such as C_(Ni)=40 wt %, the specific surface area in the mesoporous of the aluminum oxide support is decreased, resulting in the less amount of CO adsorbed to the catalyst, so that the metal surface area is deceased.

TABLE 3 The specific surface area, the pore size and the metal surface area of the Ni@Al₂O₃ Ni@Al₂O₃ S_(BET) (m²/g) d_(pore) (nm) S_(msa) (m²/g) Example 1 192.8 12.6 2.0 ± 0.6 Example 2 178.7 11.2 4.1 Example 3 166.0 11.0 4.4 Example 4 105.6 10.8 0.88 ± 0.06

Please refer to FIG. 4, which is a H₂-TPR profile of the Ni@Al₂O₃ with the different Ni concentrations. As shown in FIG. 4, four types of the reduction peaks are identified as a Ni₂O₃ peak, an α peak, a β peak and a γ peak. The first reduction peak located at T_(sur)=240° C. is the Ni₂O₃ peak. The second reduction peak located at T_(sur)=300° C. is the α peak, that is, the surface of NiO is bound to oxygen and dispersed at the surface of the aluminum oxide support. The third reduction peak located at T_(sur)=400° C. is the β peak, that is attributed to the reduction of oxygen in the surface of NiO. The fourth reduction peak located at T_(sur)=600° C. is the γ peak, that is attributed to the reduction of the bulk oxygen of the NiO particle. The results indicate that increasing C_(Ni) can increase the amount of oxygen on the surface of the catalyst, and can be confirmed by the peak area of the Ni₂O₃ peak, the α peak and the β peak.

1.2 an Effect of the Ce Concentration Loading on the Material Properties of the Ni—CeO₂@Al₂O₃

Example 5 to Example 8 of the present disclosure are based on the 15 wt % Ni concentration, and the Ce concentration is adjusted to observe the effect of the Ce concentration loading on the material properties of the Ni—CeO₂@Al₂O₃. The controlling conditions of the Ni—CeO₂@Al₂O₃ are shown in Table 4, and Comparative Example 1 of Table 4 is the CeO₂@Al₂O₃. The CeO₂@Al₂O₃ is without adding Ni and used for comparing Example 5 to Example 8, wherein C_(Ni) and C_(Ce) represent the concentrations of Ni and Ce, T_(d2) represents the second calcining temperature, and T_(pas) represents the surface passivation temperature.

TABLE 4 The controlling conditions of the Ni—CeO₂@Al₂O₃ Ni—CeO₂@Al₂O₃ C_(Ni) (wt %) C_(Ce) (wt %) T_(d2) (° C.) T_(pas) (° C.) Example 5 15 2.5 400 N/A Example 6 15 7.5 400 N/A Example 7 15 15 400 N/A Example 8 15 25 400 N/A Comparative 0 7.5 400 N/A Example 1

Please refer to FIGS. 5A and 5B. FIG. 5A is an XRD diffractogram of the Ni—CeO₂@Al₂O₃ with the different Ce concentrations. FIG. 5B is a FESEM image of the Ni—CeO₂@Al₂O₃ with the different Ce concentrations. As shown in FIG. 5A, the crystalline phase of metallic Ni is presented in Example 2 and Example 5 to Example 8, while the crystalline phase of CeO₂ is presented in Example 6 to Example 8 and Comparative Example 1. The crystallite sizes of CeO₂ (d_(CeO2)) of Example 5 to Example 8 and Comparative Example 1 are shown in Table 5. As shown in FIG. 5B, the Ni—CeO₂ particles are dispersed on the surface of the aluminum oxide support evenly, wherein 1 to 4 are the Ni—CeO₂@Al₂O₃ of Example 5 to Example 8, respectively. The results indicate that when C_(Ce) increases, the d_(CeO2) of the Ni—CeO₂@Al₂O₃ will increase. The d_(Ni) is maintained at 5.3+0.1 nm, and proved that the addition of CeO₂ does not affect the d_(Ni) Furthermore, C_(Ce) of Example 5 is too low to identify the crystalline phase and crystallite size of CeO₂ by XRD diffraction.

TABLE 5 The crystallite sizes of CeO₂ of the Ni—CeO₂@Al₂O₃ Ni—CeO₂@Al₂O₃ d_(ceO2) (nm) Example 5 N/A Example 6 4.1 Example 7 15.1 Example 8 15.3

Furthermore, the analysis of the specific surface area (S_(BET)), the pore size (d_(pore)) and the metal surface area (S_(msa)) of Example 5 to Example 8 are shown in Table 6. As shown in Table 6, C_(Ni) is maintained at 15 wt % and by increasing C_(Ce), the specific surface area of the Ni—CeO₂@Al₂O₃ is deceased from 182.9 m²/g to 112.7 m²/g, and the metal surface area is deceased from 3.4±0.56 m²/g to 1.8 m²/g. The results indicate that the decrease of the specific surface area is attributed to the increase of C_(Ce) so as to cause the deposition of Ce in the mesoporous of the aluminum oxide support. Furthermore, in the case of the addition of CeO₂, the specific surface area in the mesoporous of the aluminum oxide support is decreased, resulting in the less amount of CO adsorbed to the catalyst, so that the metal surface area is deceased.

TABLE 6 The specific surface area, the pore size and the metal surface area of the Ni—CeO₂@Al₂O₃ Ni—CeO₂@Al₂O₃ S_(BET) (m²/g) d_(pore) (nm) S_(msa) (m²/g) Example 5 182.9 11.8 3.4 ± 0.56 Example 6 159.8 12.0 2.8 Example 7 132.3 11.2 1.9 Example 8 112.7 11.0 1.8

Please refer to FIG. 6, which is a H₂-TPR profile of the Ni—CeO₂@Al₂O₃ with the different Ce concentrations. As shown in FIG. 6, four types of the reduction peaks are identified as a Ni₂O₃ peak, an α peak, a β and CeO₂ peak and a γ peak. T_(sur) of Example 5 to Example 8 in FIG. 6 is slightly lower than that of Example 1 to Example 4 in FIG. 4. Further, by increasing C_(Ce), the intensity ratio of (the Ni₂O₃ peak+the α peak) to (the β and CeO₂ peak+the γ peak) is increased, indicating that the highly-dispersed NiO in the Ni—CeO₂@Al₂O₃ is increased. The results indicate that the Ni—Ce—O interface formed by adding CeO₂ is beneficial to improve the reducibility of Ni and is the critical factor to the catalytic performance.

1.3 an Effect of the Second Calcining Temperature and the Passivation Step on the Material Properties of the Ni@Al₂O₃

Example 2 and Example 9 of the present disclosure are based on the 15 wt % Ni concentration, and the second calcining temperature is adjusted to evaluate the effect of the second calcining temperature on the material properties of the Ni@Al₂O₃. Furthermore, Example 10 is prepared by introducing the air to perform the passivation step at 200° C. after the second calcining step of Example 3. The controlling conditions of the Ni@Al₂O₃ are shown in Table 7, wherein C_(Ni) and C_(Ce) represent the concentrations of Ni and Ce, T_(d2) represents the second calcining temperature, and T_(pas) represents the surface passivation temperature.

TABLE 7 The controlling conditions of the Ni@Al₂O₃ Ni@Al₂O₃ C_(Ni) (wt %) C_(Ce) (wt %) T_(d2) (° C.) T_(pas) (° C.) Example 2 15 0 400 N/A Example 3 25 0 400 N/A Example 9 15 0 250 N/A Example 10 25 0 400 200

Please refer to FIG. 7A, which is an XRD diffractogram of the Ni@Al₂O₃ according to Example 2, Example 3, Example 9 and Example 10 of the present disclosure. As shown in FIG. 7A, only the crystalline phase of NiO is presented in Example 9, and the crystallite size of NiO (d_(NiO)) is 8.0 nm. When T_(d2) is increased to 400° C., such as Example 2, the crystalline phase of metallic Ni is presented, and the crystallite size of Ni (d_(Ni)) is 5.3 nm. The results indicate that when T_(d2) is raised to 400° C., NiO is reduced to metallic Ni. Furthermore, the crystalline phase of metallic Ni is presented in Example 10, and the crystallite size of Ni (d_(Ni)) is 7.3 nm. However, the crystallite size of Ni (d_(Ni)) of Example 3 is 7.2 nm, proved that the passivation step does not affect the d_(Ni) of Example 3.

1.4 an Effect of the Second Calcining Temperature and the Passivation Step on the Material Properties of the Ni—CeO₂@Al₂O₃

Example 6 and Example 11 of the present disclosure are based on the 15 wt % Ni concentration, and the 7.5 wt % Ce concentration. The second calcining temperature is adjusted to evaluate the effect of the second calcining temperature on the material properties of the Ni—CeO₂@Al₂O₃. Furthermore, Example 12 is prepared by introducing the air to perform the passivation step at 200° C. after the second calcining step of Example 6. The controlling conditions of the Ni—CeO₂@Al₂O₃ are shown in Table 8, wherein C_(Ni) and C_(Ce) represent the concentrations of Ni and Ce, T_(d2) represents the second calcining temperature, and T_(pas) represents the surface passivation temperature.

TABLE 8 The control conditions of the Ni—CeO₂@Al₂O₃ Ni—CeO₂@Al₂O₃ C_(Ni) (wt %) C_(Ce) (wt %) T_(d2) (° C.) T_(pas) (° C.) Example 6 15 7.5 400 N/A Example 11 15 7.5 250 N/A Example 12 15 7.5 400 200

Please refer to FIG. 7B, which is an XRD diffractogram of the Ni—CeO₂@Al₂O₃ according to Example 6, Example 11 and Example 12 of the present disclosure. As shown in FIG. 7B, the crystalline phases of NiO and CeO₂ are presented in Example 11, and the crystallite sizes of NiO (d_(NiO)) and CeO₂ (d_(CeO2)) are 5.3 nm and 9.9 nm, respectively. When T_(d2) is increased to 400° C., such as Example 6, the crystalline phase of NiO is disappeared and the crystalline phase of metallic Ni is presented, the crystallite sizes of Ni (d_(Ni)) and CeO₂ (d_(CeO2)) are 5.3 nm and 4.1 nm, respectively. The results indicate that when T_(d2) is raised to 400° C., NiO is reduced to metallic Ni. Furthermore, the crystalline phase of NiO is presented in Example 12, the crystallite sizes of Ni (d_(Ni)) and NiO (d_(NiO)) are 5.3 nm and 4.4 nm, respectively, proved that the passivation step does not affect the d_(Ni) of Example 6.

Please refer FIG. 8, which is a H₂-TPR profile of the Ni@Al₂O₃ and the Ni—CeO₂@Al₂O₃ after the passivation step. As shown in FIG. 8, four types of the reduction peaks are identified as a Ni₂O₃ peak, an α peak, a β and CeO₂ peak and a γ peak. T_(sur) of the Ni₂O₃ peak and the α peak of Example 10 and Example 12 are higher than those of Example 3 and Example 6, respectively. The results indicate that Ni on the surface of the catalyst is changed after the second calcining step at the second calcining temperature of 400° C. followed by the passivation step.

2. Reductive Amination Reaction of Polypropylene Glycol

The heterogeneous nickel-based catalyst on the aluminum oxide support of the present disclosure is performed the reductive amination reaction of polypropylene glycol step of the step 220 of the method for synthesizing polyetheramine 200 as shown in FIG. 2. In a 250 mL autoclave reaction system, the temperature is maintained at 230° C., the pressure is maintained at 1800 psi for 2 hours. Next, the feed is added, which includes 10 g polypropylene glycol, hydrogen and ammonia. The molar ratio of hydrogen to polypropylene glycol is 1.3, and the molar ratio of ammonia to polypropylene glycol is 40.6. Then, the product is heated at 130° C. of the oil bath under an atmospheric condition so as to remove water and unreacted ammonia.

Please refer to FIG. 9, which is a schematic view for the reaction mechanism of the reductive amination reaction of polypropylene glycol catalyzed by the Ni@Al₂O₃, and includes the steps 1 to 5. The step 1: a competitive adsorption of PPG and ammonia occurs toward the surface of Ni. The step 2: the alkyl group of PPG dehydrogenates to ketone. The step 3: the dehydrogenated PPG reacts with liquid ammonia to form polyimine via the condensation reaction. The step 4: polyimine reacts with the adsorbed hydrogen to form polyetheramine. The step 5: polyetheramine is desorbed from the surface of Ni. Here, the active site of the reductive amination reaction of polypropylene glycol catalyzed by the Ni@Al₂O₃ is mainly located at the surface of Ni.

Please refer to FIG. 10, which is a schematic view for the reaction mechanism of the reductive amination reaction of polypropylene glycol catalyzed by the Ni—CeO₂@Al₂O₃, and includes the steps 1 to 5. The step 1: PPG adsorbs to the surface of the Ni—CeO₂@Al₂O₃. The step 2: PPG interacts with oxygen vacancy on the surface of CeO₂ to promote the dehydrogenation at the interface of Ni—CeO₂. The step 3: ammonia simultaneously adsorbs to the surface of Ni, and after the condensation reaction, the dehydrogenated PPG reacts with liquid ammonia to form polyimine. The step 4: polyimine reacts with the adsorbed hydrogen to form polyetheramine. The step 5: polyetheramine is desorbed from the surface of Ni. Here, the interface of Ni—Ce—O provides the additional active sites for the dehydrogenation of PPG, which will reduce the impact of the strong competitive adsorption of ammonia at the surface of Ni with PPG. Besides, the desorption of polyetheramine is enhanced by CeO₂, and CeO₂ also inhibits the formation of Ni₃N on the surface of Ni.

3. The Activity Test of the Heterogeneous Nickel-Based Catalyst on the Aluminum Oxide Support 3.1 the Activity Test of the Ni@Al₂O₃ with the Ni Concentration

Please refer to FIGS. 11A, 11B and 11C. FIG. 11A is a histogram for the conversion ratio of PPG of the Ni@Al₂O₃ according to Example 1 to Example 4 of the present disclosure. FIG. 11B is a histogram for the turnover frequency of the Ni@Al₂O₃ according to Example 1 to Example 4 of the present disclosure. FIG. 11C is a histogram for the selectivity to primary amine of the Ni@Al₂O₃ according to Example 1 to Example 4 of the present disclosure. As shown in FIG. 11A, when the Ni concentration (C_(Ni)) is increased from 5 wt % to 40 wt %, the conversion ratio of PPG (X_(PPG)) is increased from 48.7% to 69.0%, and then tends to be stable. The result indicates that when C_(Ni) increases, the active surface area (S_(msa)) of the Ni@Al₂O₃ is increased so as to cause X_(PPG) increases. As shown in FIG. 11B, when the Ni concentration (C_(Ni)) is increased from 5 wt % to 40 wt %, the turnover frequency (TOF) of the Ni@Al₂O₃ is reduced from 1.15×10⁻³ s⁻¹ to 0.20×10⁻³ s⁻¹. The result indicates that when C_(Ni) increases, the Ni atom per unit mass on the surface of Ni of the Ni@Al₂O₃ is decreased so as to cause TOF of the Ni@Al₂O₃ decreases. As shown in FIG. 11C, the selectivity to primary amine (Z_(PA)) of Example 1 to Example 4 is as high as 98.8% to 99.8%.

3.2 the Activity Test of the Ni—CeO₂@Al₂O₃ with the Ce Concentration

Please refer to FIGS. 12A, 12B and 12C. FIG. 12A is a histogram for the conversion ratio of PPG of the Ni—CeO₂@Al₂O₃ according to Example 2, Example 5 to Example 8 of the present disclosure. FIG. 12B is a histogram for the turnover frequency of the Ni—CeO₂@Al₂O₃ according to Example 2, Example 5 to Example 8 of the present disclosure. FIG. 12C is a histogram for the selectivity to primary amine of the Ni—CeO₂@Al₂O₃ according to Example 2, Example 5 to Example 8 of the present disclosure. As shown in FIG. 12A, when the Ce concentration (C_(Ce)) is increased from 0 wt % to 15 wt %, the conversion ratio of PPG (X_(PPG)) is increased from 64.5% to 74.4%. As shown in FIG. 12B, when the Ce concentration (C_(Ce)) is increased from 0 wt % to 15 wt %, the turnover frequency (TOF) of the Ni—CeO₂@Al₂O₃ is increased from 0.51×10⁻³ s⁻¹ to 0.59×10⁻³ s⁻¹. The result indicates that when C_(Ce) is less than or equal to 15 wt %, the catalytic activity of the Ni—CeO₂@Al₂O₃ is proportional to C_(Ce). Therefore, the CeO₂ co-catalyst is added to form the interface of Ni—Ce—O, which provides a synergistic reaction to promote the desorption of PEA and enhances the activity of the Ni—CeO₂@Al₂O₃. As shown in FIG. 12C, the selectivity to primary amine (Z_(PA)) of Example 5 to Example 8 is as high as 99.5% to 100%. Furthermore, X_(PPG) and TOF of the Ni—CeO₂@Al₂O₃ are decreased when C_(Ce) increased from 15 wt % to 25 wt %, which is attributed to the excessive loading of CeO₂ on the surface of the Ni—CeO₂@Al₂O₃.

3.3 the Activity Test of the Nickel-Based Catalyst on the Aluminum Oxide Support with the Second Calcining Temperature

Please refer to FIGS. 13A, 13B and 13C. FIG. 13A is a histogram for the conversion ratio of PPG and the selectivity to primary amine of the Ni@Al₂O₃ according to Example 2 and Example 9 of the present disclosure. FIG. 13B is a histogram for the conversion ratio of PPG and the selectivity to primary amine of the Ni—CeO₂@Al₂O₃ according to Example 6, Example 11 and Example 12 of the present disclosure. FIG. 13C is a histogram for the conversion ratio of PPG and the selectivity to primary amine of the Ni@Al₂O₃ according to Example 3 and Example 10 of the present disclosure. As shown in FIG. 13A, when the second calcining temperature of the Ni@Al₂O₃ is decreased from 400° C. to 250° C., X_(PPG) is decreased from 64.8% to 46.2%. As shown in FIG. 13B, when the second calcining temperature of the Ni—CeO₂@Al₂O₃ is decreased from 400° C. to 250° C., X_(PPG) is decreased from 71.2% to 26.7%. The results indicate that the oxidation state of the active compound is a critical factor to catalyze the reductive amination reaction. As shown in FIG. 13C, X_(PPG) of Example 10 is close to X_(PPG) of Example 3, and X_(PPG) of Example 12 is close to X_(PPG) of Example 6. The results indicate that the surface passivation of the catalyst will not reduce the activity of the catalyst, and the Z_(PA) is also as high as 98% to 100%.

4. The Stability Test of the Heterogeneous Nickel-Based Catalyst on the Aluminum Oxide Support

Please refer to FIGS. 14A and 14B. FIG. 14A is an XRD diffractogram of the Ni@Al₂O₃ after the reductive amination reaction. FIG. 14B is an XRD diffractogram of the Ni—CeO₂@Al₂O₃ after the reductive amination reaction. As shown in FIG. 14A, the crystalline phase of metallic Ni is presented in Example 2 to Example 4, Example 9 and Example 10, and the crystallite sizes of Ni (d_(Ni)) of Example 2 to Example 4 are 28.1 nm, 26.4 nm and 24.9 nm, respectively. The results indicate that after the reductive amination reaction, the crystallite sizes of Example 2 to Example 4 are increased, and showing the sintering of Ni. Furthermore, the crystalline phase of Ni₃N is presented in Example 2, Example 4, Example 9 and Example 10, and the crystallite sizes of Ni₃N (d_(Ni3N)) are between 9.4 nm and 10.5 nm, which is attributed to the strong adsorption of ammonia on the metal surface especially in a hydrogen-deficient condition. However, during the reaction, the nitridation reaction is considered as a catalyst deactivation pathway, which reduces the yield and the selectivity by the generation of unwanted side products.

As shown in FIG. 14B, the crystalline phase of metallic Ni and CeO₂ are presented in Example 5 to Example 8, Example 11 and Example 12, and the crystallite sizes of Ni (d_(Ni)) of Example 5 to Example 8 are 15.9 nm, 25.0 nm, 17.7 nm and 18.5 nm, respectively. The results indicate that after the reductive amination reaction, the crystallite sizes of Example 5 to Example 8 are increased, and showing the sintering of Ni. However, the extent of sintering is significantly reduced through the addition of CeO₂ compared with the crystallite sizes of the Ni@Al₂O₃. Furthermore, the crystalline phase of Ni₃N is unable to clearly identified in Example 5 to Example 8, Example 11 and Example 12. Note that the addition of CeO₂ will inhibit the formation of Ni₃N.

Please refer to FIGS. 15A and 15B. FIG. 15A is a histogram for the conversion ratio of PPG and the selectivity to primary amine from the first and the second test according to Example 2 of the present disclosure. FIG. 15B is a histogram for the conversion ratio of PPG and the selectivity to primary amine from the first and the second test according to Example 6 of the present disclosure. As shown in FIG. 15A, X_(PPG) of Example 2 is 60.4% after the second test, which is 6% lower than that of the first test, and Z_(PA) is maintained at 99% after the second test. As shown in FIG. 15B, compared with the first test, X_(PPG) of Example 6 is maintained at 70.9% after the second test, and Z_(PA) is also maintained at 100% after the second test. The results indicate that the addition of CeO₂ will improve the stability of the Ni@Al₂O₃ to catalyze the reductive amination reaction of the polypropylene glycol, and the stability is improved by adding CeO₂ to inhibit the formation of Ni₃N and the sintering of the crystalline phase of metallic Ni.

Furthermore, the comparison results of the heterogeneous nickel-based catalyst on the aluminum oxide support of the present disclosure and Raney nickel catalyst are shown in Table 9. Comparative Example 2 and Comparative Example 3 are the experimental results of Raney nickel catalyst under the same conditions of the synthesis method of polyetheramine of the heterogeneous nickel-based catalyst on the aluminum oxide support. As shown in Table 9, X_(PPG) of the heterogeneous nickel-based catalyst on the aluminum oxide support of Example 2 and Example 6 is much higher than that of Raney nickel catalyst of Comparative Example 2 and Comparative Example 3 at the same conditions of the synthesis method of polyetheramine. The results indicate that the heterogeneous nickel-based catalyst on the aluminum oxide support of the present disclosure has the good high catalytic activity, and can be used to catalyze the reductive amination reaction of polypropylene glycol to synthesize polyetheramine.

TABLE 9 The comparison of the heterogeneous nickel-based catalyst on the aluminum oxide support and Raney nickel catalyst Comparative Comparative Example 2 Example 6 Example 2 Example 3 PPG feed (g) 10 10 10 10 Temperature (° C.) 230 230 200 230 Pressure (psig) 1800 1800 1850 1900 Reaction time (hr) 2 2 2 2 NH₃/PPG 40.6 40.6 40.6 40.6 H₂/PPG 1.3 1.3 1.3 1.3 Conversion (%) 64.5 66.8 21.4 25.5 TOF (10⁻⁴ s⁻¹) 5.10 5.30 0.42 0.50

In conclusion, the method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support and the heterogeneous nickel-based catalyst on the aluminum oxide support thereof of the present disclosure, which can be used for catalyzing the reductive amination reaction of polypropylene glycol are provided. Through the method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support of the present disclosure, the concentration, the composition, the second calcining temperature and the passivation temperature of the catalyst can be adjusted to improve the catalytic activity, the stability and the selectivity of the catalyst. It is effectively applied to catalyze the reductive amination reaction of polypropylene glycol so as to synthesize polyetheramine.

Although the present disclosure has been described in considerable detail with reference to certain embodiments thereof, other embodiments are possible. Therefore, the spirit and scope of the appended claims should not be limited to the description of the embodiments contained herein.

It will be apparent to those skilled in the art that various modifications and variations can be made to the structure of the present disclosure without departing from the scope or spirit of the disclosure. In view of the foregoing, it is intended that the present disclosure cover modifications and variations of this disclosure provided they fall within the scope of the following claims. 

What is claimed is:
 1. A method for fabricating a heterogeneous nickel-based catalyst on an aluminum oxide support, comprising: performing a solution preparation step, wherein a catalytically active precursor is used as a precursor solution, and the precursor solution contains a nickel ion; performing a drop-cast step, wherein the precursor solution is dropped on a support so as to obtain a catalyst precursor, and the support is an aluminum oxide support; performing a first calcining step, wherein the catalyst precursor is calcined so as to obtain an oxidation state catalyst; and performing a second calcining step, wherein the oxidation state catalyst is calcined under a reducing gas so as to obtain the heterogeneous nickel-based catalyst on the aluminum oxide support, and the reducing gas is hydrogen.
 2. The method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support of claim 1, wherein the catalytically active precursor is a nickel nitrate solution or a cerium nitrate solution, and the precursor solution is the nickel nitrate solution or a mixed solution of nickel nitrate and cerium nitrate.
 3. The method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support of claim 1, wherein the support is dried at a temperature of 353 K to 393 K first, and reserved overnight.
 4. The method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support of claim 1, wherein a temperature of the first calcining step ranges from 300° C. to 400° C.
 5. The method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support of claim 1, wherein a temperature of the second calcining step ranges from 250° C. to 400° C.
 6. The method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support of claim 1, further comprising a passivation step, wherein the passivation step is performed by introducing an air so as to passivate the heterogeneous nickel-based catalyst on the aluminum oxide support at a temperature of 180° C. to 220° C.
 7. The method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support of claim 6, wherein the passivation step further comprises cooling the heterogeneous nickel-based catalyst on the aluminum oxide support at the temperature of 200° C. to 400° C. with nitrogen.
 8. A heterogeneous nickel-based catalyst on an aluminum oxide support fabricated by the method for fabricating the heterogeneous nickel-based catalyst on the aluminum oxide support of claim
 1. 9. The heterogeneous nickel-based catalyst on the aluminum oxide support of claim 8, wherein the heterogeneous nickel-based catalyst on the aluminum oxide support further comprises a co-catalyst.
 10. The heterogeneous nickel-based catalyst on the aluminum oxide support of claim 9, wherein the co-catalyst is cerium oxide.
 11. The heterogeneous nickel-based catalyst on the aluminum oxide support of claim 10, wherein the heterogeneous nickel-based catalyst on the aluminum oxide support is a nickel catalyst on the aluminum oxide support or a nickel-cerium oxide catalyst on the aluminum oxide support.
 12. The heterogeneous nickel-based catalyst on the aluminum oxide support of claim 11, wherein a range of a nickel concentration of the nickel catalyst on the aluminum oxide support is greater than 0 wt % and less than or equal to 40 wt %.
 13. The heterogeneous nickel-based catalyst on the aluminum oxide support of claim 11, wherein the range of the nickel concentration of the nickel-cerium oxide catalyst on the aluminum oxide support is greater than 0 wt % and less than or equal to 25 wt %, and a range of a cerium concentration is greater than 0 wt % and less than or equal to 25 wt %.
 14. A method for synthesizing polyetheramine, comprising: providing the heterogeneous nickel-based catalyst on the aluminum oxide support of claim 8; and performing a reductive amination reaction of polypropylene glycol step, wherein polypropylene glycol is performed the reductive amination reaction by the heterogeneous nickel-based catalyst on the aluminum oxide support used as a catalyst so as to obtain polyetheramine at an environment contained hydrogen and ammonia.
 15. The method for synthesizing polyetheramine of claim 14, wherein a molar ratio of hydrogen to polypropylene glycol ranges from 1 to 1.5.
 16. The method for synthesizing polyetheramine of claim 14, wherein a molar ratio of ammonia to polypropylene glycol ranges from 38 to 40.6. 